MONEL-400 has a wide range of mechanical properties that vary according to the supply condition, with exceptional properties at sub-zero temperatures. Even when cooled to the temperature of liquid drogen, it does not undergo a ductile-to-brittle transition.
| Element | Min | Max |
|---|---|---|
| C | - | 0.03 |
| Mn | - | 2.0 |
| Si | - | 0.5 |
| S | - | 0.024 |
| Ni | 63.0 | - |
| Cu | 28.0 | 34.0 |
| Fe | - | 2.5 |
| - | % | % |
| Condition | Tensile(PSI(MPA)) | Yield(0.2% offset),(PSI(MPA)Min) | Elongation in 2"or 4Dm in % | Elongation 5.65√S0 min % | Rockwell Hardness HRC Max | |
|---|---|---|---|---|---|---|
| Hot worked and annealed | 70,000 (483) | 25,000 (172) | 35 | 35 | 35 | |
| Cold worked and stress relieved | ≤40 mm dia | 87,000 (600) | 60,000 (415) | 22 | 20 | 35 |
| >40mm ≤ 55mm dia | 84,000 (580) | 55,000 (380) |